Imec and AIXTRON Demonstrate 200 mm GaN Epitaxy on AIX G5+ C for 1200V Applications with Breakdown in Excess of 1800V

Vertikaler Pufferleckstrom in Durchlassrichtung, gemessen an 1200V GaN-on-QST® bei zwei verschiedenen Temperaturen: (links) 25°C und (rechts) 150°C. Der 1200V-Puffer von Imec zeigt einen vertikalen Leckstrom unter 1µA/mm2 bei 25°C und unter 10µA/mm2 bei 150°C bis zu 1200V mit einem Durchbruch von über 1800V sowohl bei 25°C als auch bei 150°C, was ihn für die Verarbeitung von 1200V-Bauteilen geeignet macht. / Vertical forward buffer leakage current measured on 1200V GaN-on-QST® at two different temperatures: (left) 25°C and (right) 150°C. Imec’s 1200V buffer shows vertical leakage current below 1µA/mm2 at 25°C and below 10µA/mm2 at 150°C up to 1200V with a breakdown in excess of 1800V both at 25°C and 150°C, which makes it suitable for the processing of 1200V devices.

Imec, a world-leading research and innovation hub in nanoelectronics and digital technologies, and AIXTRON, the leading provider of deposition equipment for compound semiconductor materials, have demonstrated epitaxial growth of gallium-nitride (GaN) buffer layers qualified for 1200V applications on 200mm QST® substrates, with a hard breakdown exceeding 1800V. The manufacturability of 1200V-qualified buffer layers opens doors to highest voltage GaN-based power applications such as electric cars, previously only with feasible silicon-carbide (SiC)-based technology. The result comes after the successful qualification of AIXTRON’s G5+ C fully automated metal-organic chemical vapor deposition (MOCVD) reactor at imec, Belgium, for integrating the optimized material epi-stack.

Wide-bandgap materials gallium-nitride (GaN) and silicon-carbide (SiC) have proved their value as next-generation semiconductors for power-demanding applications where silicon (Si) falls short. SiC-based technology is the most mature, but it is also more expensive. Over the years tremendous progress has been made with GaN-based technology grown on for example 200mm Si wafers. At imec, qualified enhancement mode high-electron-mobility transistors (HEMTs) and Schottky diode power devices have been demonstrated for 100V, 200V and 650V operating voltage ranges, paving the way for high-volume manufacturing applications. However, achieving operating voltages higher than 650V has been challenged by the difficulty of growing thick-enough GaN buffer layers on 200mm wafers. Therefore, SiC so far remains the semiconductor of choice for 650-1200V applications – including for example electric cars and renewable energy.

For the first time, imec and AIXTRON have demonstrated epitaxial growth of GaN buffer layers qualified for 1200V applications on 200mm QST® (in SEMI standard thickness) substrates at 25°C and 150°C, with a hard breakdown exceeding 1800V. Denis Marcon, Senior Business Development Manager at imec: “GaN can now become the technology of choice for a whole range of operating voltages from 20V to 1200V. Being processable on larger wafers in high-throughput CMOS fabs, power technology based on GaN offers a significant cost advantage compared to the intrinsically expensive SiC-based technology.”

Key to achieving the high breakdown voltage is the careful engineering of the complex epitaxial material stack in combination with the use of 200mm QST® substrates, executed in scope of the IIAP program The CMOS-fab friendly QST® substrates from Qromis have a thermal expansion that closely matches the thermal expansion of the GaN/AlGaN epitaxial layers, paving the way for thicker buffer layers – and hence higher voltage operation.

Dr. Felix Grawert, CEO and President of AIXTRON “The successful development of imec’s 1200V GaN-on-QST® epi-technology into AIXTRON’s MOCVD reactor is a next step in our collaboration with imec. Earlier, after having installed AIXTRON G5+C at imec’s facilities, imec’s proprietary 200mm GaN-on-Si materials technology was qualified on our G5+ C high-volume manufacturing platform, targeting for example high-voltage power switching and RF applications and enabling our customer to achieve a rapid production ramp-up by pre-validated available epi-recipes. With this new achievement, we will be able to jointly tap into new markets.” Currently, lateral e-mode devices are being processed to prove device performance at 1200V, and efforts are ongoing to extend the technology towards even higher voltage applications. Next to this, imec is also exploring 8-inch GaN-on-QST® vertical GaN devices to further extend the voltage and current range of GaN-based technology.